EN10083-2 C50, C50E Steel Plate

Katalor

  • EN10083-2 C50, C50E Steel Plate0
  • EN10083-2 C50, C50E Steel Plate1
Наведите на изображение, чтобы его увеличить
30-03-19
US $1 000,00 / Т
1,00 Т
L/C, T/T
standard exporting package
21 день(ни).

Данные Товара

C50 / C50E material is medium carbon steel with high strength steel. It is usually used in normalizing, quenching or tempering condition. C50 / C50E grade steel is used in the manufacture of mechanical products and spring pieces, such as forging gear, tie rod, roller, shaft, friction plate, agricultural spindle dig plowshares and heavy-duty spindle bearing,etc. C45, C50E steel plates are also with high wear resistance property.
Chemical Composition of EN10083-2: C50/ C50E Steel:
C: 0.47-0.55,
Si: 0.4, Mn: 0.6-0.9, P: 0.03, S: 0.035, Cr: 0.4, Mo: 0.1, Ni: 0.4
Mechannical Properties in quenching and tempering condition (room temperature):
C50/ C50E: diameter≤16mm or thickness≤8mm:
Tensile strength σb (MPa):750-900
Yield strength σs (MPa):≥520
Elongation δ5 (%):≥13
C50/ C50E: 16mm < diameter≤40mm or 8mm < thickness≤20mm:
Tensile strength σb (MPa):700-850
Yield strength σs (MPa):≥460
Elongation δ5 (%):≥15
C50/ C50E: 40mm < diameter≤100mm or 20mm < thickness≤60mm:
Tensile strength σb (MPa):650-800
Yield strength σs (MPa):≥400
Elongation δ5 (%):≥16
Recommended temperature in heat treatment: Normalizing: 830℃,Quenching:830℃, tempering 600℃
Equivalent material: SAE J403 1050 steel, JIS G4051 S50C steel
Delivery condition of C50/ C50E steel: heat treatment (Q+T, annealing, normalizing or high temperature tempering) , without heat treatment.
Katalor Amber
SHANGHAI KATALOR ENTERPRISES CO., LTD
E-mail: service8(at)katalor(dot)com
asteelgrade(at)gmail.com
Skype: klsteelamber


Смотреть Больше

Подтверждающие Документы

Деловые Данные

28-03-2019
Shanghai Katalor Enterprises Co., Ltd was founded in 1998, which has early achieved the steel structure qualification ce...
Отправить эту страницу: