Trademark B-A
Chemical composition %,max
C 0.003 Si 0.01 Mn 0.20 P 0.012 S 0.006 Al 0.15-0.50 Cr 0.02 Ni 0.01 Cu 0.02
Trademark B-AA
Chemical composition %,max
C 0.002 Si 0.006 Mn 0.12 P 0.007 S 0.001 Al 0.15-0.50 Cr 0.02 Ni 0.01 Cu 0.005
Trademark B-B
Chemical composition %,max
C 0.003 Si 0.01 Mn 0.13 P 0.009 S 0.006 Al 0.03 Cr 0.01 Ni 0.01 Cu 0.02
Trademark B-C
Chemical composition %,max
C 0.002 Si 0.01 Mn 0.03 P 0.006 S 0.005 Al 0.01 Cr 0.01 Ni 0.01 Cu 0.01
Type mm :
Medium p
late and steel billet 8-250 ,plate coil 12-25 ,straight round steel dia6.5-dia300 ,round steel coil,cold drawn plate coil 0.5-2.5 tube,etc.
We can produce the special type which you ask
application of trademark B-A:
a.make it in electric core.heel piece, gag bit in electric appliance device,telecommunication
b.Electric core of electric iron
c.Electromagnetic part of instruments and meters
d.Iron core and shell of direct-current dynamo
e.Electric part or magnetic part for car,tractor,lathe
f.Magnetic shielding apparatus
Charateristic
1 .good electromagnet character.Coercive force(Hc)low,high magnetic permeability. high saturation induction density Bs .stable magnet and no magnetic aging
2 high pure,electric pure iron,is full killed steel,refine,so the density is high,average,good,little gas, this is a reliable condition that customer simplify and cut down the anneal process of the parts.
3 cold drawn,hot roll,forge.Cold process,these is no problem such as lathe,drill,punch,bend,drawn.Hot process,such as forge,roll,there is little redsear sensibility,it is a good condition for doing in a large degree scope.
International standard
trademark coercive force Hc A/m oe
not more than coercive force aging Hc A/m oe
not more than Max.magnetic conductivity H/m Gs/Oe * not less than magnetic strength T Gs not less than
B-A 48.0 0.6 4.8 0.06 11.3
9000 B200 B300 B500 B1000 B2500 B5000 B10000
1.20
12000 1.30
13000 1.40
14000 1.50
15000   1.62
16200 1.71
17100  1.80
18000
magnetic aging:keep 100 degree for 100 hours or Condition is 790 degree after 2 hours, after cooling with the furnace.
Appliance of trademark from B-B to B-C :
The raw material of all kinds precise alloy(super alloy),electric alloy,soft magnet,amorphous alloy and permanent magnet such as NdFeB etc.


Смотреть Больше

Подтверждающие Документы

Подтверждающие документы не найдены.

Деловые Данные

3-09-2016
High purity iron billet,electric steel, electric magnetic iron, ultra low carbon magnetic iron bar,soft magnetic iron ba...
Отправить эту страницу: